RT2180

  • Appearance: White
  • Viscosity: 8000 cps at 375*F
  • Softening Point: 318*F
  • Density: .85 -.88 grams/cc
  • 35 - 50 lb box
  • 350 lb fiber drum
  • Good initial tack
  • Minimal residual tack
  • Excellent cohesion
  • Quick open time (<5 seconds)
  • High tensile strength
  • Appliction temperature: 325* to 375*F

RT2535

  • Appearance: White
  • Viscosity: 3500 cps at 375*F
  • Softening Point: 270*F
  • Density: .85 -.88 grams/cc
  • 35 - 50 lb box
  • 350 lb fiber drum
  • High initial tack
  • Good cohesion
  • Medium open time (60 seconds)
  • Excellent thermal stability @ 375*F after at least 48 hours
  • Low tensile strength
  • Application temperature: 325* to 375*F

RT2730

  • Appearance: White
  • Viscosity: 3000 cps at 375*F
  • Softening Point: 230*F
  • Density: .85 -.88 grams/cc
  • 35 - 50 lb box
  • 350 lb fiber drum
  • High initial tack
  • Good cohesion
  • Long open time (300 seconds)
  • Excellent thermal stability @ 375*F after at least 48 hours
  • Low tensile strength
  • Application temperature: 275* to 375*F

E101

  • Appearance: White
  • Viscosity: 2000 cps at 375*F
  • Softening Point: 220*F
  • Density: .85 -.88 grams/cc
  • 35 - 50 lb box
  • 350 lb fiber drum
  • High initial tack
  • Good cohesion
  • Very long open time (900 seconds)
  • Excellent thermal stability @ 375*F after at least 48 hours
  • Low tensile strength
  • Application temperature: 275* to 375*F

Description

REXtac polymers are an essential filling and flooding compound for copper and fiber optic telecommunication cables. Their inherent moisture resistance properties prevent water penetration into the inner insulation, protecting the core of the cable, and inhibiting corrosion. REXtac APAOs can sustain a wide range of temperatures while also acting as a cushion and lubricant to protect the cable from damage caused by bending and mechanical handling.